تهیه و بررسی خواص پلیمری نانو الیاف الکتروریسی شده توسط عنوان مواد ضد باکتری بالقوه

Preparation and Characterization of Polymeric Nanofibers by Electrospinning as Potential Antibacterial Materials

نویسندگان

این بخش تنها برای اعضا قابل مشاهده است

ورودعضویت
اطلاعات مجله sciencepg
سال انتشار 2017
فرمت فایل PDF
کد مقاله 25645

پس از پرداخت آنلاین، فوراً لینک دانلود مقاله به شما نمایش داده می شود.

اضافه‌کردن به سبدخرید

چکیده (انگلیسی):

Quaternized PDMAEMA (qPDMAEMA) was used to prepare nanofibers by electrospinning. At first the DMAEMA monomer was quaternized using Hexyl, dodecyl and hexadecyl bromide. Then the quaternized DMAEMA was polymerized by free radical polymerization. This polymer was characterized by 1HNMR, GPC, and thermal analysis (DSC and TGA). The (qPDMAEMA) was blended with PVA in different ratios (20/80, 25/75 and 50/50). The antibacterial properties of the prepared blends were examined against two strains type, the gram positive M. luteus and the gram negative E.coli. The antimicrobial activity showed that all blends with different alkyl side chain length (i.e. 6, 12, and 16) are highly active against M. luteus and no growth of the bacteria was observed after incubation period of 96 h, but in case of E. coli, the antibacterial activity is different. The blend having short alkyl side chain (6) are very active and can kill all the bacteria colonies. Blends that contain longer side chains are mostly inactive. However the blend compositions of PVA/PDMAEMA-12 (80/20 and 75/25) exhibit a good antimicrobial effect against E. Coli. The minimum bactericidal concentration (MBC) was obtained by determining the minimum polymer concentration at which no growth was observed. qPDMAEMA based fibers were produced using a solution blend of PDMAEMA and PVA. The quaternized PDEAMMAs/PVA blends were electrospun in ethanol. The concentration of the polymer was as high as 20% in order to get fibers. The diameter of formed fibers was found to be around 500 nm.

کلمات کلیدی مقاله (فارسی):

نانو الیاف، PDMAEMA، الکترواسپینینگ، Antibaterial پلیمرها، رایگان پلیمریزاسیون رادیکال

کلمات کلیدی مقاله (انگلیسی):

Nanofibers, PDMAEMA, Electrospinning, Antibaterial Polymers, Free Radical Polymerization